B602P POE Solar Film
- B602P is a fast-curing, UV-cut POE encapsulation film with excellent moisture barrier performance, weather resistance, PID resistance, and peel strength retention. It is suitable for high-reliability PV modules such as dual-glass modules.
- With <30% transmittance at 280–380 nm, >91% transmittance at 380–1100 nm, and glass peel strength above 100 N/cm, B602P delivers UV protection, high light transmission, strong adhesion, and efficient lamination performance.
Get a Free Consultation
Get a Free Consultation
|
Product Specifications |
||
|
Specifications |
Normal Specifications | Customized Specifications |
|
Thickness |
0.45mm – 0.65mm | 0.2 – 0.8mm |
|
Width |
1000 – 1030mm | 300 – 1300mm |
|
Length |
350m | 150m/350m/400m |
|
Technical Properties |
|||
|
Item |
Test Standard | B602P | |
|
Using Instruction |
/ | Cut-Off | |
|
Shrinkage Ratio |
MD | GB/T29848 | <3.0% |
| TD | GB/T29848 | <1.5% | |
|
Light Transmittance |
280 – 380nm | Betterial | <30% |
| 380 – 1100nm | GB/T29848 | >91% | |
|
Peel Strength |
POE/Glass | GB/T29848 | >100N/cm |
| POE/Backsheet | GB/T29848 | >70N/cm | |
|
Crosslink Degree |
GB/T29848 | >75% | |
|
Volume Resistivity |
GB/T29848 | >1*10^15 Ω·cm | |
|
Damp Heat Test |
GB/T29848 | <3.0 ΔYI | |
|
UV Aging Test |
GB/T29848 | <3.0 ΔYI | |
|
Laminating Process |
||||
|
Laminated Parameters |
Temperature(℃) | Vacuum Time(S) | Lamination Time(S) | |
|
Single Chamber Laminator |
142 – 148 | 300 – 360 | 1080±120 | |
|
Double Chamber Laminator |
Cavity 1 | 120±10 | 300±60 | 240±60 |
| Cavity 2 | 145±10 | 10 – 30 | 540±60 | |